Usoro maka ike ike ígwè bụ H. Dị ka usoro ule siri ike dị iche iche si dị, ihe nnọchianya ndị a na-ahụkarị gụnyere Brinell (HB), Rockwell (HRC), Vickers (HV), Leeb (HL), Shore (HS) hardness, wdg, n'ime ha. A na-ejikarị HB na HRC eme ihe. HB nwere ọtụtụ ngwa ngwa, na HRC dabara adaba maka ihe ndị nwere isi ike dị elu, dị ka ike ọgwụgwọ okpomọkụ. Ihe dị iche bụ na ihe ntinye nke ihe nleba anya siri ike dị iche. Onye na-anwale ike ike Brinell bụ onye na-enyocha bọl, ebe onye na-anwale hardness Rockwell bụ ihe nrịbama diamond.
HV-adabara maka nyocha microscope. Vickers hardness (HV) Pịa elu ihe ahụ nwere ibu na-erughị 120kg yana indenter square square diamond nwere akụkụ vertex nke 136°. A na-ekewa mpaghara elu nke olulu ntinye ihe site na uru ibu, nke bụ Vickers hardness value (HV). A na-egosipụta ike ike Vickers dị ka HV (na-ezo aka GB/T4340-1999), ọ na-atụkwa ihe nlele dị oke mkpa.
Ihe nlebanya ike ike HL dị mma maka nha. Ọ na-eji isi bọọlụ mmetụta na-emetụta elu ike siri ike wee mepụta bounce. A na-agbakọ ike siri ike site na nha nke nkwụghachi ọsọ nke ntụmadị na 1mm site na nlele elu ruo n'ọsọ mmetụta. Usoro a bụ: Leeb hardness HL=1000×VB (ọsọ nlọghachi)/VA (ọsọ mmetụta).
Enwere ike ịtụgharị ihe nleba anya Leeb siri ike ka ọ bụrụ Brinell (HB), Rockwell (HRC), Vickers (HV), Shore (HS) ike ka emechara nlele Leeb (HL). Ma ọ bụ jiri ụkpụrụ Leeb jiri Brinell (HB), Rockwell (HRC), Vickers (HV), Leeb (HL), Shore (HS) tụọ uru ịdị ike ozugbo.
HB - Brinell siri ike:
A na-ejikarị brinell hardness (HB) eme ihe mgbe ihe dị nro, dị ka ọla ndị na-adịghị ferrous, ígwè tupu ọgwụgwọ okpomọkụ ma ọ bụ mgbe annealing gasịrị. A na-ejikarị Rockwell hardness (HRC) eme ihe maka ihe ndị nwere isi ike dị elu, dị ka isi ike mgbe ọgwụgwọ okpomọkụ gasịrị, wdg.
Brinell hardness (HB) bụ ibu ule nke otu nha. A na-agbanye bọọlụ nchara siri ike ma ọ bụ bọọlụ carbide nke otu dayameta n'elu igwe a ga-anwale. A na-edobe ibu ule maka oge a kapịrị ọnụ, wee wepụ ibu ahụ iji tụọ dayameta nke ntinye n'elu a ga-anwale. The Brinell hardness uru bụ quotient nwetara site na-ekewa ibu site Spherical elu ebe nke indentation. N'ozuzu, a na-agbanye bọọlụ ígwè siri ike nke ụfọdụ nha (na-abụkarị 10mm na dayameta) n'ime ihe dị n'elu ihe na-ebu ibu (na-emekarị 3000kg) ma na-echekwa ya ruo oge ụfọdụ. Mgbe e wepụrụ ibu ahụ, oke ibu ahụ na mpaghara ntinye bụ uru Brinell hardness (HB), na unit ahụ bụ kilogram ike / mm2 (N / mm2).
Rockwell hardness na-ekpebi index uru ike siri ike dabere na nrụrụ rọba dị omimi nke ntinye. A na-eji 0.002 mm mee ihe dị ka ihe siri ike. Mgbe HB> 450 ma ọ bụ ihe nlele ahụ pere mpe, enweghị ike iji ule siri ike nke Brinell wee jiri nha Rockwell hardness kama. Ọ na-eji cone diamond nwere akụkụ vertex nke 120 ° ma ọ bụ bọọlụ nchara nke nwere dayameta nke 1.59 ma ọ bụ 3.18mm iji tinye n'elu ihe a na-anwale n'okpuru ụfọdụ ibu, na-agbakọ ike nke ihe ahụ site na omimi. nke indentation. Dị ka ike nke ihe nnwale ahụ si dị, a na-egosipụta ya na nha atọ dị iche iche:
HRA: Ọ bụ ike nke enwetara site na iji 60kg ibu na diamond cone indenter, nke a na-eji maka ihe ndị nwere oke siri ike (dị ka carbide cimented, wdg).
HRB: Ọ bụ ike nke enwetara site n'iji ibu 100kg na bọọlụ siri ike nke nwere dayameta nke 1.58mm, nke a na-eji maka ihe ndị nwere ike dị ala (dị ka ígwè annealed, nkedo ígwè, wdg).
HRC: Ọ bụ ike nke enwetara site na iji ibu 150kg na diamond cone indenter, nke a na-eji maka ihe ndị nwere oke siri ike (dị ka ígwè siri ike, wdg).
Na mgbakwunye:
1.HRC pụtara Rockwell hardness C scale.
A na-eji 2.HRC na HB eme ihe n'ọtụtụ ebe.
3.HRC ọdabara nso HRC 20-67, dakọtara na HB225-650,
Ọ bụrụ na isi ike dị elu karịa nke a, jiri Rockwell hardness A scale HRA,
Ọ bụrụ na isi ike dị ala karịa nke a, jiri Rockwell hardness B scale HRB,
Oke elu nke Brinell hardness bụ HB650, nke enweghị ike ịdị elu karịa uru a.
4.Indenter nke Rockwell hardness tester C scale bụ cone diamond nwere akụkụ vertex nke ogo 120. Ibu ule bụ uru ụfọdụ. Ọkọlọtọ China bụ 150 kgf. Ihe nnwapụta nke Brinell hardness tester bụ bọọlụ nchara siri ike (HBS) ma ọ bụ bọọlụ carbide (HBW). Ibu ule dịgasị iche na dayameta nke bọọlụ ahụ, sitere na 3000 ruo 31.25 kgf.
5.The Rockwell hardness indentation dị nnọọ obere, na a tụrụ uru na- localized. Ọ dị mkpa iji tụọ ọtụtụ isi iji chọta nkezi uru. Ọ dabara maka ngwaahịa emechara na mpekere dị mkpa ma bụrụ nkewa dị ka nnwale na-adịghị emebi emebi. The Brinell ekweghị ekwe indentation bụ ibu, tụrụ atụ bụ ezi, ọ bụghị adabara okokụre ngwaahịa na mkpa Mpekere, na n'ozuzu na-adịghị nkewa dị ka ndị na-adịghị ebibi ule.
6. Uru ike nke Rockwell hardness bụ ọnụ ọgụgụ na-enweghị aha na-enweghị nkeji. (Ya mere, ọ bụ ihe na-ezighi ezi ịkpọ Rockwell hardness dị ka ogo ụfọdụ.) Uru siri ike nke Brinell hardness nwere nkeji ma nwee ụfọdụ mmekọrịta dị nso na ike nkwụsị.
7. Rockwell hardness na-egosipụta ozugbo na ọkpụkpọ ma ọ bụ gosipụtara n'ụdị dijitalụ. Ọ dị mfe ịrụ ọrụ, ngwa ngwa na nghọta, ma dabara adaba maka mmepụta oke. Isi ike brinell chọrọ microscope iji tụọ dayameta indentation, wee lelee tebụl ma ọ bụ gbakọọ, nke na-akawanye njọ ịrụ ọrụ.
8. N'okpuru ọnọdụ ụfọdụ, HB na HRC nwere ike gbanwee site na-ele anya na tebụl. Enwere ike ịdekọ usoro mgbako echiche dịka: 1HRC≈1/10HB.
Nnwale ike siri ike bụ ụzọ nnwale dị mfe ma dị mfe na nnwale akụrụngwa. Iji jiri ule siri ike dochie ụfọdụ nnwale akụrụngwa, a chọrọ mmekọrịta ngbanwe ziri ezi n'etiti ike na ike na mmepụta.
Omume egosila na enwere mmekọrịta dị nso n'etiti ụkpụrụ isi ike dị iche iche nke ihe igwe yana n'etiti uru ike na uru ike. N'ihi na a na-ekpebi uru ike siri ike site na nkwụsi ike nrụrụ plastik nke mbụ na nkwụsi ike nke nrụrụ plastik na-aga n'ihu, ike dị elu nke ihe ahụ, na-eme ka nkwụsị nke nrụrụ plastik dị elu, na ọnụ ahịa siri ike dị elu.
Oge nzipu: Ọgọst-16-2024